Pengaruh Kuat Arus Listrik Pengelasan Terhadap Kekerasan Lapisan Lasan pada Baja ASTM A316

 http://dx.doi.org/10.21831/dinamika.v3i1.19109

Dody Prayitno(1*), Harry Daniel Hutagalung(2), Daisman P.B. Aji(3),

(1) Teknik Mesin, Universitas Trisakti
(2) Teknik Mesin, Universitas Trisakti
(3) Teknik Mesin, Universitas Trisakti
(*) Corresponding Author

Abstract


Seat and plug are components of control valve that are always in friction contact. The plug usually wears out. One of the efforts in battling this wear is hardfacing, a process of cladding the base metal to increase its surface hardness using SMAW. This research is aimed to investigate the effect of welding current on weld surface hardness. The experiments used stainless steel (ASTM A316) for the plug materials and Stellite 6, which was an electrode with 3.2 mm in diameter, for the filler metal. Flat welding position was used. The current was varied from 120 A to 140 A and then to 160 A. Results of the hardness tests done on the weld surface show that when the welding current was increased from 120 A to 140 A, it increased the surface hardness from 465 HV to 514.7 HV. Subsequent current increase from 140 A to 160 A decreased the surface hardness from 514.7 HV to 423 HV.

Sebuah control valve memiliki seat dan plug yang selalu bergesekan, sehingga plug sering mengalami keausan. Salah satu upaya untuk mengurangi keausan dengan cara hardfacing, yaitu penambahan material (cladding) pada logam induk dengan maksud meningkatkan kekerasan permukaan. Penambahan material dapat dilakukan dengan pengelasan SMAW, dimana salah satu parameter yang berpengaruh terhadap kekerasan lapisan lasan adalah besarnya arus listrik pengelasan. Tujuan penelitian adalah untuk mengetahui pengaruh arus listrik pengelasan terhadap kekerasan lapisan lasan. Metode penelitian dimulai dengan menyiapkan baja tahan karat (ASTM A316) digunakan sebagai material plug dan material stillite 6 sebagai material penambah yang berupa berupa elektroda berdiameter 3.2 mm. Pengelasan dengan posisi datar dengan variasi arus pengelasan adalah 120 A, 140 A dan 160 A. Hasil pengujian kekerasan menunjukkan bahwa peningkatan arus lasan dari 120 A ke 140 A meningkatkan kekerasan permukaan lasan  dari 465 HV menjadi 514.7 HV. Peningkatan arus lasan berikutnya dari 140 A ke 160 A menyebabkan terjadinya penurunan kekerasan permukaan lasan dari 514.7 HV menjadi 423 HV.


Keywords


: las SMAW, stellite 6, kekerasan, kuat arus listrik, pengelasan, heat-affected zone

Full Text:

Fullpaper

Article Metrics

Abstract views : 88 | views : 92

References


Linconn Electric Company (2014), “Hardfacing product and procedure Selection,” Bucklet, diakses tanggal 26 November 2017 dari http://www.lincolnelectric.com

ISA Interchange (2017), “Autoquiz20150612”, diakses tanggal 26 Oktober 2017 dari https://automation.isa.org/2015/06/what-is-the-process-of-grinding-the-plug-and-seat-of-a-valve-called/autoquiz20150612/

M. Yogi Nasrul L., Heru Suryanto, Abdul Qolik (2016), “ Pengaruh Variasi Arus Las Smaw Terhadap Kekerasan Dan Kekuatan Tarik Sambungan Dissimilar Stainless Steel 304 Dan St 37, Jurnal Teknik Mesin, No. 1, April 2016, Hal 1-12 , diakses tanggal 10 novemer 2017 dari https://www.researchgate.net/publication/315779962_PENGARUH_VARIASI_ARUS_LAS_SMAW_TERHADAP_KEKERASAN_DAN_KEKUATAN_TARIK_SAMBUNGAN_DISSIMILAR_STAINLESS_STEEL_304_DAN_ST_37

Ridway Balaka, Abd. Kadir, Dedi Saputra Tolantomo(2016), “Analisis Pengaruh Arus Pengelasan Pada Sudut Elektroda 70° Terhadap Sifat Kekerasan Dan Struktur Mikro Baja Karbon Rendah Menggunakan Jig Welding”, Jurnal Enthalpy – E-ISSN :2502-8944, Vol. 2, No.2 November 2016 hal 50-55 . diakses tanggal 10 novemver 2047 dari http://www.Ojs.Uho.Ac.Id/Index.Php/Enthalpy/Article/Download/1775/1256.

American Society of Materials International (1993), ASM Handbook Vol. 8: Mechanical Testing and Evaluation, ASM International, United State of America.

Davis, J.R., Hardfacing (1993), Weld Cladding, and Dissimilar Metal Joining. ASM Handbook Vol. 6: Welding, Brazing and Soldering (pp.1967- 2061). ASM International.

Delero (2017), “STELLITE TM 6 ALLOY,” techincal data diakses tanggal 11 november 2017 dari https://deloro-test-bed.squarespace.com/s/Deloro-MDS-Stellite6-rev00.pd

Suratman, M. (2001),” Teknik Mengelas Asetilen, Brazing dan Busur Listrik, Pustaka Grafika, Bandung..

Joko Santoso, (2006), ” Pengaruh Arus Pengelasan Terhadap Kekuatan Tarik Dan Ketangguhan Las Smaw Dengan Elektroda E7018”, Skripsi, Universitas Negeri Semarang,

Trinova Budi Santoso, Solichin, Prihanto Tri Hutomo, (2015), “ Pengaruh Kuat Arus Listrik Pengelasan Terhadap Kekuatan Tarik Dan Struktur Mikro Las Smaw Dengan Elektroda E7016, Jurnal Teknik Mesin, Tahun 23, No. 1, April 2015, Hal 59- 64

A. S. Mohruni, B. H. Kembaren, (2013) “Pengaruh Variasi Kecepatan Dan Kuat Arus Terhadap Kekerasan, Tegangan Tarik, Struktur Mikro Baja Karbon Rendah Dengan Elektroda E6013”, Jurnal Rekayasa Mesin Vol. 13 No. 1 Maret 2013, Hal 1-8,

Wiryosumarto, H dan Okumura, T, (2008) Teknologi Pengelasan Logam. PT. Pradnya Paramitha, Jakarta,




 http://dx.doi.org/10.21831/dinamika.v3i1.19109

Refbacks

  • There are currently no refbacks.


Jurnal ini terindex di :

ISSN 2548-7590 (ONLINE)

ISSN 2598-392X (PRINTED)


Lisensi Creative Commons 
Jurnal Dinamika Vokasional Teknik Mesin by http://journal.uny.ac.id/index.php/dynamika was distributed under a Creative Commons Attribution 4.0 International License.


 

View My Stats