SYNTHESIS OF MEMBRANES FROM PILLARED CLAY FeCl3 FOR SEAWATER DESALINATION APPLICATION
Adi Darmawan, Master Program of Chemistry, Faculty of Sciences and Mathematics, Diponegoro University, Semarang, Indonesia, Indonesia
RA. Lusiana, Master Program of Chemistry, Faculty of Sciences and Mathematics, Diponegoro University, Semarang, Indonesia, Indonesia
Abstract
Synthesis of membranes has been done using pillared clay FeCl3for desalination application. Pillared clays FeCl3were synthesized via a sol-gel method using [OH] / [Fe] 0.25, 0.5, 1, 2, 2.5. Formed sol-gel was furnace on 600oC for 2 hours. The membranes which were cooled at room temperature for 3 days then tested filtration of seawater. The results showed that membrane pillared clays FeCl3 with a ratio [OH] / [Fe] 0.25 reached filtration purity 99.99% with the initial TDS 27.58 ppm and resulted rejection TDS 00.22 ppm after filtration. Membrane with ratio [OH] / [Fe] 0.5 reached filtration purity 80%, with initial TDS 27.58 ppm and resulted rejection TDS 11.76 ppm, while membranes with ratio [OH] / [Fe] 1,2 and 2,5 was broken during the filtration proces, its resulted very small rejection.
Keywords: membrane, pillared clay, FeCl3, Seawater desalination
Keywords
Full Text:
PDFReferences
Huang, A., N. Wang, and J. Caro, Seeding-free synthesis of dense zeolite FAU membranes on 3-aminopropyltriethoxysilane - functionalized alumina supports. Journal of Membrane Science, 2011. 389: p. 272-279.
Franken, A., M. Mulder, and C. Smolders, Pervaporation process using a thermal gradient as the driving force. Journal of Membrane Science, 1990. 53(1-2): p. 127-141.
Srinivasan, R., Advances in Application of Natural Clay and Its Composites in Removal of Biological, Organic, and Inorganic Contaminants from DrinkingWater. Advances in Materials Science and Engineering, 2011. Article ID 872531,: p. 17.
Molina, C., et al., A comparison of Al-Fe and Zr-Fe pillared clays for catalytic wet peroxide oxidation. Chemical Engineering Journal, 2006. 118(1): p. 29-35.
HR1, Y. and I.P. , Agus Prasetya, Kartika U, PEMBUATAN DAN KARAKTERISASI AMPO TERPILAR BESI OKSIDA [KAJIAN RASIO HIDROLISIS AGEN PEMILAR (OH/Fe]. Prosiding Seminar Nasional Teknik Kimia “Kejuangan”, Yogyakarta, 26 Januari 2010.
P. Bankovic¤, A.M.-N., N. Jovic-Jovi•cic, J. Dostanic, •Z. •Cupic, and D.L.c.c.a.D. Jovanovic, Synthesis, Characterization and Application of Al,Fe-Pillared Clays. ACTA PHYSICA POLONICA A, 2009. Vol. 115 (4): p. 5.
Carriazo, J., R. Molina, and S. Moreno, A study on Al and Al–Ce–Fe pillaring species and their catalytic potential as they are supported on a bentonite. Applied Catalysis A: General, 2008. 334(1): p. 168-172
REDJEKI,S., DESALINASI DENGAN MEMBRAN. 2011: p. 215.
Masturi, S., et al., Permeability, strength and filtration performance for uncoated and titania-coated clay wastewater filters. American Journal of Environmental Sciences, 2012. 8(2): p. 79-94.
Rosadalima, D., Modifikasi Bentonit terpilar Al dengan Kitosan untuk Adsorpsi Ion Logam Berat. Jurnal FMIPA UI, (6), 2012: p. 1-10.
DOI: https://doi.org/10.21831/jsd.v7i1.22260
Refbacks
- There are currently no refbacks.
Copyright (c) 2018 Muslimin Muslimin, Adi Darmawan, RA. Lusiana