ANALYSIS OF SMAW IN DIFFERENT MATERIALS WITH ELECTRODE VARIATIONS

Dede Ardi Rajab, STT Wastukancana Purwakarta, Indonesia
Lapi Artitana, STT Wastukancana Purwakarta, Indonesia
Agus Suprayitno, STT Wastukancana Purwakarta, Indonesia

Abstract


Welding is a technique for joining metals by melting part of the parent metal and filler metal with or without additional metal and producing a continuous connection. One type of welding that is often used is SMAW welding (Shield Metal Arc Welding). In SMAW welding, the influence of the electrode strength or amperage used plays an important role in welding, because it influences the results of the joint strength during welding. Therefore, the current setting must be appropriate to the material and choosing the right welding parameters will also improve the quality of the welding results. This research was conducted to determine the mechanical properties of tensile testing and the microstructure of the influence of the different electrodes and amperes that will be used. In this research, current variations of 70 A, 80 A, and 90 A were used and the types of electrodes used were E6013, E309-16 and E7018. The research results obtained from the tensile test had an optimum value for the E7018 electrode, 90 A with a tensile strength of 41 .60 kg/mm. The tensile test results for E7018 obtained an average tensile value of 33.19 kg/mm. The tensile test result value of E6013, 80 ampere has a value of 36.55 kg/mm, after being averaged the tensile strength of E6013 is 35.36 kg/mm, the tensile test result of E309, 80 A has a value of 38.15 kg/mm after being averaged got a tensile test value of 36.20 kg/mm.


Full Text:

113-124 (PDF)

References


Afan, M. Bin, Purwantono, P., Mulianti, M., & Rahim, B. (2020). Pengaruh Suhu Penyimpanan Elektroda Low Hydrogen E7016 terhadap Hasil Uji Tekuk Sambungan Las Pelat Baja Karbon SS400. Jurnal Rekayasa Mesin, 15(1), 20. https://doi.org/10.32497/jrm.v15i1.1823

Amanda, Prasetyo, A., Kasir, & Faisal, Arfi, R. (2011). Pengaruh Kekuatan Tarik Sambungan Pengelasan Dissimilar Smaw Dengan Bentuk Kampuh V Groove Variasi Arus 50 Ampere , 70 Ampere , 100 Ampere.

Arifin, J., Purwanto, H., & Syafa’at, I. (2017). Pengaruh Jenis Elektroda Terhadap Sifat Mekanik Hasil Pengelasan. Momentum, 13(1), 27–31.

Azwinur, A., Jalil, S. A., & Husna, A. (2017). Pengaruh variasi arus pengelasan terhadap sifat mekanik pada proses pengelasan SMAW. Jurnal POLIMESIN, 15(2), 36. https://doi.org/10.30811/jpl.v15i2.372

Gunawan, Y., Endriatno, N., & Anggara, B. H. (2017). Analisa Pengaruh Pengelasan Listrik Terhadap Sifat Mekanik Baja Karbon Rendah Dan Baja Karbon Tinggi. Enthalpy-Jurnal Ilmiah Mahasiswa Teknik Mesin, 2(1), 1–12.

Iswanto, P. T., Mudjijana, & Himarosa, R. A. (2017). Karakterisasi Sambungan SMAW Baja Karbon Rendah Menggunakan 3 Jenis Elektroda. Material Dan Proses Manufaktur, 1(2), 103–109.

Jordi, M., Yudo, H., & Jokosisworo, S. (2017). Analisa Pengaruh Proses Quenching Dengan Media Berbeda Terhadap Kekuatan Tarik dan Kekerasan Baja St 36 Dengan Pengelasan SMAW. Jurnal Teknik Perkapalan, 5(4), 785. http://ejournal3.undip.ac.id/index.php/naval

Kurniawan, I., Budiarto, U., & Mulyatno, I. P. (2018). Analisa Kekuatan Puntir, Kekuatan Tarik, Kekerasan dan Uji Metalografi Baja S45C Sebagai Bahan Poros Baling-Baling Kapal (Propeller Shaft) Setelah Proses Tempering. Jurnal Teknik Perkapalan, 6(1), 313–322.

M, L. N. Y., Heru, S., & Abdul, Q. (2016). Pengaruh Variasi Arus Las Smaw Terhadap Kekerasan Dan Kekuatan Tarik Sambungan Dissimilar Stainless Steel 304 Dan St 37. Jurnal Teknik Mesin, 24(1), 1–12. http://journal2.um.ac.id/index.php/jurnal-teknik-mesin/article/view/511

Mawahib, M. Z., Jokosisworo, S., & Yudo, H. (2017). Pengujian Tarik Dan Impak Pada Pengerjaan Pengelasan SMAW Dengan Mesin Genset Menggunakan Diameter Elektroda Yang Berbeda. Kapal: Jurnal Ilmu Pengetahuan Dan Teknologi Kelautan, 14(1), 26–32. https://doi.org/10.14710/kpl.v14i1.15533

Mesin, S. T., Teknik, F., Surabaya, U. N., Mesin, J. T., Teknik, F., & Surabaya, U. N. (2020). PENGARUH VARIASI MEDIA PENDINGIN DALAM PROSES PWHT PENGELASAN SMAW UNTUK MATERIAL BAJA SS400 TERHADAP NILAI KEKERASAN DAN KEKUATAN TARIK Canggih Wahyunanta Novi Sukma Drastiawati Abstrak.

Purwaningrum, Y. (2006). Karakterisasi Sifat Fisis Dan Mekanis Sambungan Las Smaw Baja a-287 Sebelum Dan Sesudah Pwht. Teknoin, 11(3), 233–242. https://doi.org/10.20885/teknoin.vol11.iss3.art7

Ramadhan, F., Irawan, A., & Kurniawan, F. A. (2020). Arus Pengelasan Terhadap Tarik Las SMAW Elektroda E6013 Pada Baja Karbon Rendah. Jurnal SiMeTRi Rekayasa, 2(2), 116–122.

Ritonga, A. S., & Purwaningsih, E. S. (2018). Penerapan Metode Support Vector Machine ( SVM ) Dalam Klasifikasi Kualitas Pengelasan Smaw ( Shield Metal Arc Welding ). Ilmiah Edutic, 5(1), 17–25.

Romdhoni, V. Y. F., Fadelan, F., & Winardi, Y. (2019). Pengaruh Heat Input Terhadap Hasil Kekuatan Sambungan Pengelasan Smaw Pada Material Stainless Steel 201. Komputek, 3(2), 14. https://doi.org/10.24269/jkt.v3i2.256

Setiawan, J., & Sungkono. (2017). Karakteristik Daktilitas Ss304 Yang Teroksidasi. Urania, 23(3), 165–174.

Soleh, A. A., Purwanto, H., & Syafa’at, I. (2017). Analisa Pengaruh Kuat Arus Terhadap Struktur Mikro, Kekerasan, Kekuatan Tarik Pada Baja Karbon Rendah Dengan Las Smaw Menggunakan Jenis Elektroda E7016. Jurnal Ilmiah Cendekia Eksakta, 1(2), 29–35.

Wijoyo, W., Albab, U., Ardika, W. T., & Darojat, M. W. (2019). Karakteristik Kekuatan Tarik Sambungan Las Tak Sejenis Baja Karbon-Stainless Steel. FLYWHEEL : Jurnal Teknik Mesin Untirta, V(1), 60. https://doi.org/10.36055/fwl.v0i0.5252

Yassyir Maulana. (2016). Analisis Kekuatan Tarik Baja St37 Pasca Pengelasan Dengan Variasi Media Pendingin Menggunakan Smaw. Jurnal Teknik Mesin UNISKA, 2(1), 1–8.




DOI: https://doi.org/10.21831/dinamika.v8i2.64465

Refbacks

  • There are currently no refbacks.


Copyright (c) 2023 Jurnal Dinamika Vokasional Teknik Mesin

Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.

Lisensi Creative Commons 

Jurnal Dinamika Vokasional Teknik Mesin by http://journal.uny.ac.id/index.php/dynamika was distributed under a Creative Commons Attribution 4.0 International License.


 

 

 

in collaboration with:

 

 

View My Stats