The Analysis of Screws Spacing Effect On The Flexural Strength Of Laminated Wood Beams From Pine Pallets Waste

Authors

  • Yudhi Arnandha Civil Engineering Department, Faculty of Engineering, Tidar University, Jl. Kapten S. Parman No. 39 Magelang 56116
  • Kadarosi Dyah Pandhini Civil Engineering Department, Faculty of Engineering, Tidar University, Jl. Kapten S. Parman No. 39 Magelang 56116
  • Ali Murtopo Civil Engineering Department, Faculty of Engineering, Tidar University, Jl. Kapten S. Parman No. 39 Magelang 56116

DOI:

https://doi.org/10.21831/inersia.v19i1.48457

Keywords:

Flexural Strength, Laminated Beams, Screw Spacing

Abstract

Pine pallets are often used to design the interior of houses, as opposed to pine waste, which is underutilized due to its reduced strength and limited size. Therefore, this research aims to optimize the use of pine pallet waste by making laminated beams using screw joints and determining the effect of screw spacing on the strong bending of laminated beams. Flexural strength tests of laminated wood beams measuring 5 cm x 5 cm x 76 cm with varying screw spacing of 4 cm, 8 cm, 12 cm, and 16 were used to conduct this research. This is in addition to screw length, head, and body diameters of 5 cm, 8 mm, and 4 mm, respectively. Strong bending testing was carried out at the Structural Laboratory of the Department of Civil Engineering, Faculty of Engineering, Tidar University, Magelang. The test results of consecutive Modulus of Rupture (MOR) had average values of 20.996 MPa, 23.067 MPa, 20.207 MPa, 19.292 MPa. and Modulus of Elasticity (MOE) of 1,352.68 MPa, 1,449.35 MPa, 1,146.76 MPa, and 1,128.90 MPa. The result showed that the use of varying screw spacing has no significant effect on the flexural strength of laminated beams. Furthermore, the laminated pine pallet waste with screws can be used as an alternative to pure wood by paying attention to the proper joint spacing.

References

Aditya, R., B., Suprapto, 2020, Pengaruh Jarak antar Paku terhadap Flexural strength Balok Kayu Laminasi Mekanik Kayu Mahoni dan Sengon, Jurnal Rekayasa Teknik Sipil 1(2), Universitas Negeri Surabaya, Surabaya.

Arnandha, Y., dkk., 2018, Studi Potensi Penggunaan Alat Sambung pada Sistem Sambungan WPC Sengon dengan WPC Jati, Universitas Gadjah Mada, Yogyakarta.

Darwis, Z., Derry, W., 2016, Pengaruh Penggunaan Pasak dengan Variasi Jarak (10 cm, 15 cm, 20 cm) terhadap Flexural strength Balok Laminasi Bambu (Dendrocalamus Asper), Jurnal Teknik Sipil 5(2), Universitas Sultan Ageng Tirtayasa, Banten.

Mahdinur, 2016, Studi Penggunaan Alat Sambung Sekrup [Ada Wood Plastic Composite (WPC) dengan Metode Geser Satu Irisan (Single Shear Connections), Skripsi Teknik Sipil, Universitas Gadjah Mada, Yogyakarta.

Metode Pengujian Flexural strength Kayu di Laboratorium, 1995, SNI 03-3959:1995, Jakarta.

Metode Pengujian Pengukuran Water content, Kayu dan Bahan Berkayu, 2002, SNI 03-6850:2002, Jakarta.

Panel Kayu - Penentuan Kerapatan, 2008, SNI ISO 9427:2008, Jakarta.

Puluhulawa, I., Alamsyah., Diana, R., 2018, Pengaruh Penambahan Baut dan Paku terhadap Flexural strength Balok Laminasi Kayu Mahang dan Meranti, Jurnal Teknik Sipil, Politeknik Negeri Bengkalis, Riau.

Safitri, R., Rachmat, G., 2016, Studi Kelayakan Kayu Bekas Landasan Peti Kemas sebagai Elemen Interior Lepas, Institut Seni Budaya Indonesia, Bandung.

Spesifikasi Desain Untuk Konstruksi Kayu, 2013, SNI 7973:2013. Jakarta.

Standard Test Methods for Mechanical Properties of Lumber and Wood-Based Structural Materials, 2009, American Society for Testing and Materials. ASTM D4761 - 05, West Conshohocke, PA : ASTM Internasional

Downloads

Published

2023-05-30

How to Cite

Arnandha, Y., Pandhini, K. D., & Murtopo, A. (2023). The Analysis of Screws Spacing Effect On The Flexural Strength Of Laminated Wood Beams From Pine Pallets Waste. Inersia : Jurnal Teknik Sipil Dan Arsitektur, 19(1), 93–102. https://doi.org/10.21831/inersia.v19i1.48457

Issue

Vol. 19 No. 1 (2023): May

Section

Articles

License

Authors who publish with INERSIA journal agree to the following terms:

  1. Authors retain copyright and grant the INERSIA journal right of first publication with the work simultaneously licensed under Creative Commons Attribution License (CC BY 4.0) that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
  2. Authors can enter into separate, additional contractual arrangements for the non-exclusive distribution of the published version of the work (e.g., post it to an institutional repository or edit it in a book), with an acknowledgment of its initial publication in this journal.
  3. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) before and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work.
Lisensi Creative Commons
INERSIA by https://journal.uny.ac.id/index.php/inersia was distributed under a Creative Commons Attribution 4.0 International License